PA66 A 218G V33 BLACK 34N法国罗地亚TECHNYL 33%玻纤增强热稳定尼龙66塑料（18024445500）
TECHNYL A 218G V33 BLACK 34N
Properties
Typical values of properties are for black grades
Standards Unit Values
d.a.m. Cond.
Physical
Water absorption(24h at 23°C) ASTM D-792 % 0,80
Density ISO 1183/A g/cm3 1,39
Molding shrinkage Parallel RHODIA % 0,40
Molding shrinkage normal or perpendicular RHODIA % 1
Mechanical
Tensile Modulus ISO 527 Type 1A MPa 11500 7900
Tensile strength at break ISO 527 Type 1A MPa 200 140
ASTM D-638 MPa 195
Elongation at break ISO 527 Type 1A % 3,40
ASTM D-638 % 3
Flexural modulus ISO 178 MPa 9500 7000
ASTM D-790 MPa 9500
Flexural maximum stress ASTM D-790 MPa 295
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 12 19
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 92 98
Izod notched impact strength (23 °C) ASTM D256 J/m 120
ISO 180/1A kJ/m2 13 20
Flammability
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 HB
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 700
Limit Oxygen Index ISO 4589 23
Thermal
Melting Temperature ISO 11357 °C 260
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 250
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 255
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 2,5
perpendicular (23°C to 85°C)
Electrical
Comparative tracking index (Sol A) IEC 60112 V 450 425
Dielectric strength IEC 60243 kV/mm 34 29
Dissipation factor IEC 60250 0,010 0,110
Relative permittivity IEC 60250 3,70 4
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 5E 14 1E 13 |