PA66 A 60G1 V25法国罗地亚TECHNYL阻燃级尼龙66塑料（18024445500）
TECHNYL A 60G1 V25
Properties
Typical values of properties are for natural grades
Standards Unit Values
d.a.m. Cond.
Physical
Water absorption(24h at 23°C) ISO 62 % 0,83
Density ISO 1183/A g/cm3 1,38
Molding shrinkage Parallel RHODIA % 0,50
Molding shrinkage normal or perpendicular RHODIA % 0,90
Molding Shrinkage Isotropy RHODIA 0,50
Mechanical
Tensile Modulus ISO 527 Type 1A MPa 9500 8000
Tensile strength at break ISO 527 Type 1A MPa 142 88
ASTM D-638 MPa 130
Elongation at break ISO 527 Type 1A % 2 2,70
ASTM D-638 % 2,80
Flexural modulus ASTM D-790 MPa 8300
Flexural maximum stress ASTM D-790 MPa 195
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 6 8
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 65 85
Charpy unnotched impact strength (-30 °C) ISO 179/1fU kJ/m2 60
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 6,8 9
ASTM D256 J/m 95
Flammability
Flammability (Thickness: 0,8 mm) ISO 1210 / UL94 V0
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 V0
Flammability (Thickness: 3,2 mm) ISO 1210 / UL94 V0
Glow Wire Flammability Index (Thickness: 0,8 mm) ISO 60695-2-12 °C 960
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 960
Glow Wire Flammability Index (Thickness: 3,2 mm) ISO 60695-2-12 °C 960
Glow Wire Ignition Temperature (Thickness: 1,6 ISO 60695-2-13 °C 775
mm)
Glow Wire Ignition Temperature (Thickness: 3,2 ISO 60695-2-13 °C 775
mm)
Limit Oxygen Index ISO 4589 33
Thermal
Melting Temperature ISO 11357 °C 263
ASTM D3417 °C 262
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 246
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 240
Heat deflection temperature (0,45 MPa) ISO 75/Bf °C 260
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 3
perpendicular (23°C to 85°C)
Melt Mass-Flow Rate (MFR) (275 °C, 0,005 kg) ISO/FDIS 1133 g/10mn 27
Electrical
Comparative tracking index (Sol A) IEC 60112 V 600 600
Dielectric strength IEC 60243 kV/mm 30 28 |